Abstract Graphene oxide (GO) is one of the main precursors for the production of graphene and other graphene-based materials. We report a simple, safe, and fast synthesis method to obtain graphene oxide as a functional material for battery-type electrodes. Washing and lyophilization processes were performed to evaluate their effects on exfoliation and removal of functional groups from graphene sheets. Sample GO1 consisted of a 10-layer stack of oxidized graphene, while sample GO2 had 8 stacked layers. The difference between them was an extra washing and lyophilization process in the GO2 sample. The electrochemical performance of graphene oxide-based electrodes, classified as battery-type, indicated an improved specific capacity of 10.15 C.g-1 for GO1 against 4.55 C.g-1 for GO2 at a specific current of 0.5 A.g-1. This superior battery-type behavior of the GO1 electrode, also confirmed by electrochemical impedance spectroscopy, was most likely due to a higher degree of oxygenated groups on its surface, as shown by energy dispersive spectroscopy (EDS) and Fourier transform infrared spectroscopy (FTIR) studies.

Resumo O fosfato tricálcico (TCP) é um biomaterial que está sendo produzido em diversas aplicações biomédicas, além de sua biocompatibilidade e capacidade osteocondutora. Polímeros biodegradáveis de origem natural ou sintética, como quitosana e poli(álcool vinílico) (PVA), vêm sendo utilizados para aplicações de engenharia de tecidos por apresentarem as propriedades da fase orgânica nativa do tecido ósseo. Desse modo, o objetivo deste trabalho foi a obtenção de filmes finos cerâmicos baseados em TCP, quitosana e PVA através do método de tape casting. Dados de viscosidade para todas as suspensões mostraram-se ideais para o processamento escolhido. As curvas termogravimétricas demonstraram perfis semelhantes e foi possível observar que com o aumento do teor de quitosana ocorreu maior perda de massa total. Reflexões de DRX relacionadas à fase β-TCP de estrutura ortorrômbica foram encontradas, evidenciando que não houve transformação de fases. A análise de MEV revelou graus de rugosidade nas superfícies dos filmes com pouca influência do aumento do conteúdo de quitosana.

Abstract Tricalcium phosphate (TCP) is a biomaterial produced in several biomedical applications, in addition to having biocompatibility and osteoconductive capacity. Biodegradable polymers of natural or synthetic origin such as chitosan and polyvinyl alcohol (PVA) have been used for tissue engineering applications because they have the properties of the native organic phase of bone tissue. Thus, the objective of this study was to obtain ceramic tapes based on TCP, chitosan, and PVA through the tape casting method. The viscosity data for all suspensions were ideal for the chosen processing. The thermogravimetric curves showed similar profiles, and it was possible to observe that a greater total mass loss occurred with the increase in the chitosan content. XRD reflections related to the β-TCP phase of the orthorhombic structure were found, showing no phase transformation. SEM analysis showed degrees of roughness on the film surfaces with little influence from the increase in chitosan content.